Cold Rolled Steel Properties 1008

Cold rolled c1008 steel is produced from rimmed capped and semi killed steel and are intended for exposed or unexposed parts involving bending moderate drawing or forming and welding.

Cold rolled steel properties 1008.

It is composed of in weight percentage 0 10 max carbon c 0 30 0 50 manganese mn 0 04 max phosphorus p 0 05 max sulfur s and the base metal iron fe. This material should be painted or plated to prevent rust. Properties of a1008 steel sheet a1008 is a standard specification for cold rolled carbon steel. Cold rolled carbon structural high strength low alloy high strength low alloy with improved formability solution hardened and bake hardenable steel sheet in coils and cut lengths.

Cold rolled steel c1008 grade summary. Astm 1008 is a low carbon steel containing approximately 0 40 manganese that has excellent weldability and formability primarily used in extruded cold. The table below shows the approximate mechanical properties corresponding to the five commercial tempers of cold rolled carbon steel strip. This table is presented as a matter of general information.

Astm a366 astm a1008 steel aisi 1008 is a standard grade carbon steel. The limits of tensile strength etc are not intended as criteria for acceptance or rejection unless specifically agreed to by the manufacturer. The process of cold rolling the sheet creates a smooth surface which is typically oiled to prevent surface rust from forming. Other designations of aisi 1008 carbon steelinclude uns g10080 and aisi 1008.

Cs type b.